Recommended products: Hydroxylamine-based phenol-free antioxidant 420 with strong color protection

Revonox 420 is a hydroxylamine-based phenol-free antioxidant with good color protection, high compatibility, low volatility and stable high-temperature storage. It performs particularly well as a stabilizer in melt processing.

It is more effective than traditional hindered phenolic antioxidants in inhibiting gas fading and discoloration. It can be used together with phosphoric acid-based antioxidants to achieve optimal performance. Revonox 420 is particularly suitable for polypropylene fibers, automotive TPO, and systems that strictly require color protection and resistance to gas fading, such as polyolefin applications.

Product Application

Revonox 420 is recommended to be used in combination with phosphite stabilizers, such as DEOX 68 and DEOX 604. This combination can be used as a stabilizer for efficient melt processing, suitable for polypropylene fiber application systems and automotive TPO. The recommended dosage is 0.05% to 0.15%, which varies depending on the material or application.

Product Features: Gas fading resistant, suitable for polyolefins such as polypropylene/polyethylene, no animal origin ingredients

Material properties

Chemical structure

Chemical name: Oxidized bis(hydrogenated tallow alkyl) amines

CAS number 143925-92-2

Molecular formula C36H75NO

Molecular weight 538

Physical data

Odor: Odorless

Melting point: 96~98 °C

Specific gravity: 0.95 (25 °C, g/mL)

Vapor pressure: 1E-10 mmHg (25 °C)

Product specifications

Appearance: Off-white~white powder

Melting point: 90 °C min.

Volatilization: 0.5% max.

Solubility (g/100 ml solvent @ 25°C)

Heptane: <0.1

Ethyl acetate: <0.1

Butanone: <0.1

Toluene: <0.1

Water: Insoluble

Performance data

PPa polymer melt stability

Number of squeezes

Control group(MFI = 5.5)

a. Polymer: Polypropylene (homo-MFI = 5.5)

b. Processing conditions: Multi-extrusion, twin-screw extruder (？ = 35 mm, L/D = 36)

C. Melt flow rate was measured by weight, at 230 ° C and 2.16 kg pressure every 10 minutes.

d. 0.1 part Revonox 420 and 0.1 part DEOX 68

PPa polymer color stability

a. Polymer: Polypropylene (homo·MFI=5.5)

b. Test conditions: Oven aging test, using a recirculating air oven at 150°C for 6 days

Packaging

 20kg/carton