Recommended products:Fenghong New Material High Viscosity Low-to-Medium-Polarity Solvent-Free Organic Bentonite FHGEL-203B
2024-02-18 17:22
The FHGEL-203B high viscosity low-to-medium-polarity solvent-free organic bentonite, launched by Fenghong New Material, is a new type of composite organic clay characterized by easy dispersion and dust-free feeding. The product is suitable for medium-to-low polarity systems and solvent-free systems, without the need for activators. It disperses simply with high-speed shear. The product exhibits strong pseudoplasticity, with high viscosity at low shear rates, excellent anti-settling properties, and rapid viscosity reduction at high shear rates, providing excellent workability during application.
Application Areas:
● Architectural coatings
● Anti-corrosion coatings
● PVC plastic solvents
● Adhesives
● Sealants
● Low-polarity industrial cleaners
Physical Properties:
Appearance |
Light yellow powder |
105°C Volatile Content, % |
≤10.0 |
Powder Fineness % ( through 325 mesh) |
≥98.0 |
LOI%(900℃/2h) |
≤35.0 |
Usage Instructions:
1) Direct Addition Method
When the mechanical stirring equipment has sufficient shear speed, or when a colloid mill is added, the following material addition sequence is recommended:
I) Resin/solvent;
II) FHGEL-203B;
III) Wetting/dispersing agent;
IV) Pigments;
V) Fillers;Key points to note for this method: It is generally not recommended to add FHGEL-203B after adding pigments, as it can affect the dispersion of FHGEL-203B in the system. FHGEL-203B follows rheological rules and is not affected by increased grinding temperatures.
2) Pre-gel Method
When there is excess solvent in the system, it is recommended to pre-gel FHGEL-203B. It is generally recommended to pre-gel at 10-15% (under conditions of high-speed dispersion). If the pre-gel needs to be pumped, solvents or wetting agents can be used to adjust the viscosity. If FHGEL-203B is pre-gelled in a solvent with a polarity that is not suitable for it, a small amount of polar activator such as water can be added. The amount of activator added should be 5-10% of the amount of FHGEL-203B.
Recommended Addition Amounts
Application Area
Recommended Addition Amount
Coating Systems
PVC Plastic Solvents
Adhesives
Sealants
Industrial Cleaners
Packaging and Storage:
The product is packaged in an outer kraft paper bag and an inner polyethylene film bag in a double-layer packaging, or valve paper bag packaging. The weight is typically 10±0.25 kg or as per customer requirements. It should be stored under dry conditions at a temperature of 0°C to 30°C. The shelf life is 24 months.
More Hzinfo
- Chitosan-based Bioadhesives: Strong Bonds for Biomedical Applications
- Chitosan-based bioadhesives show great potential in medical technology, providing safe applications for wound healing and tissue regeneration.
-
2024-11-09
- Graco Inc. Completes Acquisition of Corob S.p.A.
- Adds a global manufacturer of dispensing and mixing solutions for paints and coatings.
-
2024-11-09
- Recommended products: Hydroxylamine-based phenol-free antioxidant 420 with strong color protection
- Revonox 420 is a hydroxylamine-based phenol-free antioxidant with good color protection, high compatibility, low volatility and stable high-temperature storage.
-
2024-11-08