Water-based polymer colloids with a branched chain architecture as low-gel pressure-sensitive adhesives
2024-09-18 08:39
Researchers found that the branching of polymer chains significantly enhances the adhesive properties of pressure-sensitive adhesives.
The performance of water-based acrylic pressure-sensitive adhesives, in which the latex particles had minimal gel content of typically less than a few percent and the polymer chains had a branched architecture, were investigated. A series of semi-batch emulsion copolymerizations of 2-octyl acrylate, isobornyl acrylate and acrylic acid was carried out in the presence of ethylene glycol dimethacrylate as crosslinker.
The molecular weight distributions and branched chain topology were regulated by using 2-ethylhexyl thiogly colate as a chain-transfer agent. The monomers and chain-transfer agent were selected as these were already available as bio-based feedstocks, or had a realistic potential to become available from non-petrochemical resources. Adhesive films cast from the polymer dispersions demonstrated good peel, shear strength and tack adhesion energies. This is attributed to polymer chain branching, which unlocks a broader window for the design rules for pressure-sensitive adhesives. Detailed rheological studies of the viscoelastic materials were conducted to support the adhesive test results.
Source: Polymer Chemistry, Issue 28, 2024
More Hzinfo
- Chitosan-based Bioadhesives: Strong Bonds for Biomedical Applications
- Chitosan-based bioadhesives show great potential in medical technology, providing safe applications for wound healing and tissue regeneration.
-
2024-11-09
- Graco Inc. Completes Acquisition of Corob S.p.A.
- Adds a global manufacturer of dispensing and mixing solutions for paints and coatings.
-
2024-11-09
- Recommended products: Hydroxylamine-based phenol-free antioxidant 420 with strong color protection
- Revonox 420 is a hydroxylamine-based phenol-free antioxidant with good color protection, high compatibility, low volatility and stable high-temperature storage.
-
2024-11-08